Twinning and Slip in Zinc by Indentation
- Creators
- Blish, R. C., II
- Vreeland, T., Jr.
Chicago
An error occurred while generating the citation.
Abstract
Observations of twinning and slip deformation caused by indentation of zinc reveal that extensive slip on the basal and second-order pyramidal systems takes place at loads up to 5 kg. Prismatic punching through 1-cm crystals is observed at indentation loads in excess of about 2.5 kg. It is concluded that the stress at the tip of the twins cannot be obtained by use of an elastic stress analysis.
Additional Information
©1968 The American Institute of Physics. Received 5 December 1967. This work was supported by the U.S. Atomic Energy Commission and the California Institute of Technology.Attached Files
Published - BLIjap68a.pdf
Submitted - Twinning_and_Slip_in_Zinc_by_Indentation.pdf
Files
Twinning_and_Slip_in_Zinc_by_Indentation.pdf
Files
(4.3 MB)
| Name | Size | Download all |
|---|---|---|
|
md5:510ab6c68825068645f045edbd8ebbdc
|
3.3 MB | Preview Download |
|
md5:5733c744fb0641724193861b1b1d46c2
|
987.6 kB | Preview Download |
Additional details
- Eprint ID
- 11190
- Resolver ID
- CaltechAUTHORS:BLIjap68a
- Atomic Energy Commission
- Caltech
- Created
-
2008-07-22Created from EPrint's datestamp field
- Updated
-
2021-11-08Created from EPrint's last_modified field
- Other Numbering System Name
- CALT
- Other Numbering System Identifier
- 473-24