Poly(arylene sulfide)s by nucleophilic aromatic substitution polymerization of 2,7‐difluorothianthrene

Abstract

Poly(thianthrene phenylene sulfide) and poly(thianthrene sulfide) have been prepared by nucleophilic aromatic substitution polymerization of the activated monomer 2,7‐difluorothianthrene with bis thiophenoxide and sulfide nucleophiles, respectively. The resulting polymers are thermally stable, amorphous materials that have been characterized by differential scanning calorimetry (DSC), thermogravimetric analysis (TGA), gel permeation chromatography (GPC), matrix‐assisted laser desorption/ionization‐time‐of‐flight (MALDI‐TOF) mass spectrometry, UV‐Vis spectroscopy, refractometry, and intrinsic viscosity (IV) measurements. The polymers produced exhibit 5% weight loss values approaching 500 °C in inert and air atmospheres and glass transition temperatures that range from 149 to 210 °C. Poly(thianthrene phenylene sulfide) with a number average molecular weight of 22,100 g/mol has been synthesized with an IV in DMPU of 0.62 dL/g at 30 °C. Creasable films of this polymer have been prepared by solvent casting and melt pressing at 250 °C. Films of poly(thianthrene phenylene sulfide) exhibit transparencies greater than 50% at wavelengths exceeding 400 nm and a high refractive index value of 1.692 at a wavelength of 633 nm, making the polymer interesting for optical applications.

Additional details