The introduction of dislocations and slip bands in molybdenum single crystals
- Creators
- Lau, S. S.
- Vreeland, T., Jr.
Abstract
The characteristics of selectively introduced slip bands and individual dislocations were investigated. It was found that slip bands produced by indenting the (112) surface had three types of Burgers vectors concentrated at the two edges of the slip band while the middle of the slip band consisted of primarily the ± ½ [111] Burger's vector. Scratching the specimen with a needle almost parallel to the (112) surface in the [111] direction produced individual screw dislocations near the scratch mark. Similar scratches normal to the [111] direction produced fine slip bands with a ± 1/2 [111] Burgers vector.
Additional Information
© 1973 Wiley-VCH Verlag GmbH & Co. KGaA. Received July 17, 1973. This work was supported by the U.S. Atomic Energy Commission. CALT-767-P3-34.Attached Files
Submitted - The_Introduction_of_Dislocations_and_Slip_Bands....pdf
Files
The_Introduction_of_Dislocations_and_Slip_Bands....pdf
Files
(1.9 MB)
Name | Size | Download all |
---|---|---|
md5:efa3e520c1f724c5fec321b387348f36
|
1.9 MB | Preview Download |
Additional details
- Eprint ID
- 54723
- Resolver ID
- CaltechAUTHORS:20150211-115716594
- Atomic Energy Commission
- Created
-
2015-02-12Created from EPrint's datestamp field
- Updated
-
2021-11-10Created from EPrint's last_modified field
- Other Numbering System Name
- CALT
- Other Numbering System Identifier
- 767-P3-34