Shock induced formation of MgAl_2O_4 spinel from oxides

Abstract

The physics of mineral grain sliding, which occurs upon dynamic compression of rocks, is investigated by shock loading single crystals of corundum (Al_2O_3) and periclase (MgO) in contact obliquely in impact experiments. Energy dispersive X-ray analysis and X-ray diffraction studies of samples recovered from 26–36 GPa, 800 ns experiments indicated that under certain conditions a spinel phase of composition MgAl_2O_4 and thickness ≤20 µm was produced at the interface between the two crystals. Although the computed shock (continuum) temperatures were below those necessary to melt the initial oxides, the spinel nonetheless appears to have formed as a result of localised melting, via grain boundary sliding friction, followed by rapid quenching. Scanning electron microscopy (SEM) revealed some evidence for such melting. Moreover, the timescale of the experiments is too short for solid state diffusion (during the shock state) to explain the observed spinel thickness, although defect enhanced solid state diffusion, subsequent to loading and unloading, remains a possibility. The results also reinforce other recent observations and theories of heterogeneous deformation in minerals.

Additional Information

© 1994 by the American Geophysical Union. Paper number 94GL00079. Received August 24, 1993; revised November 30, 1993; accepted January 11, 1994. We appreciate the help of Drs. John Armstrong, Cheryl Brigham and Yuntai Sheng with the energy dispersive X-ray analysis. The constructive comments of two reviewers is greatly appreciated. Contribution #5296, Division of Geological and Planetary Sciences.

Attached Files

Published - grl7395.pdf

Files

grl7395.pdf
Files (495.6 kB)
Name Size Download all
md5:9919e2c01d2d4d41c89f957c3d706163
495.6 kB Preview Download

Additional details

Created:
August 20, 2023
Modified:
October 18, 2023