Si_3N_4 optomechanical crystals in the resolved-sideband regime
- Creators
- Davanço, M.
- Ates, S.
- Liu, Y.
- Srinivasan, K.
Abstract
We demonstrate sideband-resolved optomechanical crystals supporting 10^5 quality factor optical modes at 980 nm, coupled to GHz frequency mechanical modes with quality factors of ≈3000. Optomechanical electromagnetically induced transparency and absorption are observed at room temperature and in atmosphere with intracavity photon numbers in excess of 10^4.
Additional Information
© 2014 American Institute of Physics Publishing LLC. Received 21 November 2013; accepted 13 December 2013; published online 27 January 2014. We thank Vladimir Aksyuk and Oskar Painter for helpful discussions. This work was partially supported by the DARPA MESO program. S.A. acknowledges support under the Cooperative Research Agreement between the University of Maryland and NIST-CNST (Award No. 70NANB10H193). Y. L. acknowledges support under the NIST-ARRA Measurement Science and Engineering Fellowship Program Grant No. 70NANB10H026 through the University of Maryland.Attached Files
Published - 1.4858975.pdf
Files
1.4858975.pdf
Files
(1.5 MB)
| Name | Size | Download all |
|---|---|---|
|
md5:a58a8ba1af91eb6ea0defbba1f2debab
|
1.5 MB | Preview Download |
Additional details
- Eprint ID
- 44406
- Resolver ID
- CaltechAUTHORS:20140320-100826833
- DARPA MESO program
- University of Maryland
- 70NANB10H193
- NIST-CNST
- 70NANB10H026
- University of Maryland NIST-ARRA Measurement Science and Engineering Fellowship Program
- Created
-
2014-03-20Created from EPrint's datestamp field
- Updated
-
2021-11-10Created from EPrint's last_modified field