In-Situ Investigation of Plasticity at Nano-Scale

Abstract

Mechanical behavior of crystals is dictated by dislocation motion in response to applied force. While it is extremely difficult to directly observe the motion of individual dislocations, several correlations can be made between the microscopic stress-strain behavior and dislocation activity. Here, we present for the first time the differences observed between mechanical behavior in two fundamental types of crystals: face-centered cubic, fcc (Au, Cu, AI, Ni, etc.) and body-centered cubic, bcc (W, Cr, Mo, Nb, etc.) with sub-micron dimensions subjected to in-situ micro-compression in SEM chamber. In a striking deviation from classical mechanics, there is a significant increase in strength as crystal size is reduced to 100nm; however in gold crystals (fcc) the highest strength achieved represents 44% of its theoretical strength while in molybdenum crystals (bcc) it is only 7%. Moreover, unlike in bulk where plasticity commences in a smooth fashion, both nano-crystals exhibit numerous discrete strain bursts during plastic deformation. These remarkable differences in mechanical response of fcc and bcc crystals to uniaxial micro-compression challenge the applicability of conventional strain-hardening to nano-scale crystals. We postulate that they arise from significant differences in dislocation behavior between fcc and bcc crystals at nanoscale and serve as the fundamental reason for the observed differences in their plastic deformation. Namely, dislocation starvation is the predominant mechanism of plasticity in nano-scale fcc crystals while junction formation and subsequent hardening characterize bcc plasticity, as confirmed by the microstructural electron microscopy. Experimentally obtained stress-strain curves together with video frames during deformation and cross-sectional TEM analysis are presented, and a statistical analysis of avalanche-like strain bursts is performed for both crystals and compared with stochastic models.

Additional Information

© 2008 ASME.

Attached Files

Published - Greer_2009p519.pdf

Files

Greer_2009p519.pdf
Files (198.2 kB)
Name Size Download all
md5:bf3a43f84b380533e630fd6f71f864c9
198.2 kB Preview Download

Additional details

Created:
August 20, 2023
Modified:
October 24, 2023