Superconductivity as a Structural Characterization Tool in Amorphous Materials

Citation

Clemens, Bruce Montgomery (1983) Superconductivity as a Structural Characterization Tool in Amorphous Materials. Dissertation (Ph.D.), California Institute of Technology. doi:10.7907/GTS1-9E08. https://resolver.caltech.edu/CaltechETD:etd-09112002-182754

Abstract

This thesis presents the use of superconductivity as a structural probe for studying amorphous and metastable materials. The characteristics of the superconducting state which facilitate its use as a probe are explained, followed by a description of some of the properties of the materials studied. The superconducting measurements performed were critical current, transition temperature and upper critical field. Materials prepared by rapid quench from the melt, sputter deposition and ion beam mixing were studied. The critical current measurements performed on liquid quenched materials reflect three pinning mechanisms. Crystalline inclusions in otherwise amorphous (Mo0.6Ru0.4)80Si10B10 produced a dramatic increase in critical current. The pinning in purely amorphous (Mo0.6Ru0.4)82B18 was shown to be affected by pinning by surface roughness on the sample edges. This contribution can be eliminated by a proper sample geometry and electropolish treatment. The bulk pinning in purely amorphous (Mo0.6Ru0.4)82B18 was shown to first decrease and then increase as a function of annealing time. This reflects the disappearance of quenched in inhomogeneous strains and excess volume defects followed by the growth of an inhomogeneity such as compositional phase segregation during an anneal. The upper critical field was measured for liquid quenched (Mo0.6Ru0.4)1-xBx for x = 0.12, 0.18 and 0.22 both before and after an anneal. The annealed samples exhibited greater transition widths and more curvature in the Hc2(T) curves than the unannealed samples which are evidence for a growth of inhomogeneities upon annealing. Measurements on sputter deposited (Mo0.6Ru0.4)82B18 were performed on samples sputtered in low (5 µm) and high (75 µm) Ar pressure, The material sputtered in low Ar pressure had a greater drop in Tc than the liquid quenched material and a pinning profile which exhibited a peak near Hc2. The sample sputtered in high Ar pressure was very inhomogeneous as evidenced by transition width and flux pinning force profile. Measurements were performed on ion beam mixed Mo55Ru45. The structure consisted of an amorphous matrix with crystalline inclusions. The pinning profile was characteristic of a strong pinning mechanism. The pinning force decreased then increased as a function of ion beam dose. This reflects the destruction of the remnants of the original structure followed by the formation of an inhomogeneity such as σ-MoRu or Xe gas bubbles during ion beam irradiation.

Item Type:Thesis (Dissertation (Ph.D.))
Subject Keywords:Applied Physics
Degree Grantor:California Institute of Technology
Division:Engineering and Applied Science
Major Option:Applied Physics
Thesis Availability:Public (worldwide access)
Research Advisor(s):
  • Johnson, William Lewis
Thesis Committee:
  • McGill, Thomas C. (chair)
  • Johnson, William Lewis
  • Mercereau, James E.
  • Nicolet, Marc-Aurele
  • Vreeland, Thad
Defense Date:22 September 1982
Funders:
Funding AgencyGrant Number
Department of Energy (DOE)UNSPECIFIED
IBMUNSPECIFIED
Record Number:CaltechETD:etd-09112002-182754
Persistent URL:https://resolver.caltech.edu/CaltechETD:etd-09112002-182754
DOI:10.7907/GTS1-9E08
Default Usage Policy:No commercial reproduction, distribution, display or performance rights in this work are provided.
ID Code:3456
Collection:CaltechTHESIS
Deposited By: Imported from ETD-db
Deposited On:13 Sep 2002
Last Modified:17 Sep 2020 00:42

Thesis Files

[img]
Preview
PDF - Final Version
See Usage Policy.

5MB

Repository Staff Only: item control page