Controlled partial embedding of carbon nanotubes within flexible transparent layers

Abstract

Applications of carbon nanotubes (CNTs) like field emission displays, super-capacitors, and cell growth scaffolds can benefit from controllable embedding of the CNTs in a material such that the CNTs are anchored and protrude a desired length. We demonstrate a simple method for anchoring densely packed, vertically aligned arrays of CNTs into silicone layers using spin-coating, CNT insertion, curing, and growth substrate removal. CNT arrays of 51 and 120 µm in height are anchored into silicone layers of thickness 26 and 36 µm, respectively. Scanning electron microscopy (SEM) and optical microscopy are used to characterize the sample morphology, a 5.5 m s^-1 impinging water jet is used to apply shear stress, and a tensile test shows that the silicone layer detaches from the substrate before the CNTs are ripped from the layer. The CNTs are thus well anchored in the silicone layers. The spin-coating process gives control over layer thickness, and the method should have general applicability to various nanostructures and anchoring materials.

Files

Additional details