Pseudo-binary phase diagram for Zr-based in situ ß phase composites
Abstract
The pseudo-binary (quasi-equilibrium) phase diagram for Zr-based bulk metallic glasses with crystalline in situ precipitates (ß phase) has been constructed from high-temperature phase information and chemical composition analysis. The phase evolution was detected in situ by high-energy synchrotron x-ray diffraction followed by Rietveld analysis of the data for volume fraction estimation. The phase diagram delineates phase fields and allows the control of phase fractions. Combined with related previous work by the authors, this diagram offers a unique opportunity to control both the morphology and volume of the dendritic ß phase precipitates to enhance the properties of the composites.
Additional Information
© 2007, Materials Research Society. (Received 17 June 2006; accepted 31 October 2006) The authors would like to thank Jin-Yoo Suh at Caltech for assisting sample preparation as well as Minha Lee at Ames National Laboratory for help with SEM observation.Files
LEEjmr07.pdf
Files
(4.5 MB)
| Name | Size | Download all |
|---|---|---|
|
md5:a66a2df64e61f557c7b456356045eade
|
4.5 MB | Preview Download |
Additional details
- Eprint ID
- 7592
- Resolver ID
- CaltechAUTHORS:LEEjmr07
- Created
-
2007-03-10Created from EPrint's datestamp field
- Updated
-
2021-11-08Created from EPrint's last_modified field