Metastable phase formation in the Zr-Al binary system induced by mechanical alloying
- Creators
- Fecht, H. J.
- Han, G.
- Fu, Z.
- Johnson, W. L.
Abstract
We have studied the sequence of phase transformations induced in the Zr-Al binary system by mechanical alloying of mixed Zr and Al powders. The structure of these materials has been studied by transmission electron microscopy and by x-ray diffraction measurements. Three different metastable phases have been found experimentally with variation of the initial composition xAl: (1) a nanocrystalline supersaturated solid solution of alpha-Zr for xAl<=0.15, (2) an amorphous phase for 0.15
Additional Information
© 1990 American Institute of Physics (Received 23 June 1989; accepted 5 October 1989) The financial support by the U.S. Department of Energy (DOE Contract No. DE-FG03-86ER45242) is gratefully acknowledged. The authors are indebted to C. Garland for the TEM work and E. Hellstern, Y. Seki, and C. E. Krill III for useful discussions.Attached Files
Published - FECjap90a.pdf
Files
FECjap90a.pdf
Files
(1.2 MB)
| Name | Size | Download all |
|---|---|---|
|
md5:aa44a299f1bb29b207a033f548ecba4a
|
1.2 MB | Preview Download |
Additional details
- Eprint ID
- 5695
- Resolver ID
- CaltechAUTHORS:FECjap90a
- DE-FG03-86ER45242
- Department of Energy (DOE)
- Created
-
2006-10-27Created from EPrint's datestamp field
- Updated
-
2021-11-08Created from EPrint's last_modified field