Room Temperature Lithium Phases from Density Functional Theory

Abstract

Metallic lithium is a promising electrode material for developing next generation rechargeable batteries, but it suffers from dendrite formation upon recharging. This compromises both efficiency and safety of these systems. The surface phenomena responsible for dendrite formation are difficult to characterize experimentally making it important to use Quantum Mechanics (QM) to provide the understanding needed to design improved systems. The most accurate practical level of QM for such studies is the PBE form of density functional theory (DFT.) We report here an assessment of the accuracy for PBE to predict the most stable four phases of bulk lithium. PBE predicts three phases, bcc, fcc, and hcp, to be nearly equal in stability (within 5 meV.) Including the zero point energy and enthalpy corrections at standard conditions (298 K and 1 atm) we predict bcc most stable, fcc at 0.0029 eV, hcp at 0.0036 eV, and cI16 at 0.0277 eV. Indeed their experimental free energies under ambient conditions differ only by a few meV, with bcc considered most stable. Experimentally, the fourth phase becomes stable at high pressure (>30-40 GPa) and low temperature (<200 K.) In order to use QM calculations to predict growth mechanisms, it is essential to bias the calculations by imposing the desired crystal structure in the underlying layers. We consider that this will allow QM studies of dendritic growth to be studied in conditions far from the crystalline phase due to the lower surface energy of bcc.

Additional Information

© 2016 American Chemical Society. Publication Date (Web): November 9, 2016. This research was partially funded by a grant to Caltech from the Bosch Energy Research Network (program manager Boris Kozinsky).

Attached Files

Accepted Version - acs_2Ejpcc_2E6b08168.pdf

Supplemental Material - jp6b08168_si_001.pdf

Files

jp6b08168_si_001.pdf
Files (173.0 kB)
Name Size Download all
md5:80e2957c771ececa32ff05a5bea002a5
41.8 kB Preview Download
md5:6b44fc29326f914af643bf2bf45f73bc
131.2 kB Preview Download

Additional details

Created:
August 18, 2023
Modified:
October 23, 2023