Water adsorption on stepped ZnO surfaces from MD simulation

Abstract

This work presents a ReaxFF reactive force-field for use in molecular dynamics simulations of the ZnO– water system. The force-field parameters were fitted to a data-set of energies, geometries and charges derived from quantum-mechanical B3LYP calculations. The presented ReaxFF model provides a good fit to the QM reference data for the ZnO–water system that was present in the data-set. The force-field has been used to study how water is adsorbed, molecularly or dissociatively, at monolayer coverage on flat and stepped ZnO surfaces, at three different temperatures (10 K, 300 K, and 600 K). The stepped surfaces were created by introducing steps along the (0001)-direction on the (1010)-surface. Equilibrium between molecular and dissociated water was observed on the (1010) terraces, resulting in a half dissociated, half molecular water monolayer. The equilibrium between dissociated and molecular water on the surface was found to be reached quickly (<10 ps). When water molecules desorb and the coverage falls, the 1:1 water–hydroxyl ratio is maintained on (1010) terraces, while steps remain largely hydroxylated. The results show that structures that promote hydrogen bonding are favored and that the presence of steps promotes an increased level of hydroxylation in the water monolayers.

Additional Information

© 2009 Elsevier. Received 15 September 2009; accepted 11 December 2009. Available online 29 December 2009. This work was supported by the Swedish Research Council (VR) and by NSF Grant #DMR 0427177. Computer time was provided by SNIC. The computations were performed on UPPMAX under Project s00707-54. Many useful discussions with Dr. Tomas Edvinsson and Dr. Pavlin Mitev are acknowledged.

Additional details

Created:
August 21, 2023
Modified:
October 20, 2023